The quality of hot-dip galvanized barbed wire is only the zinc layer attached to the surface of the wire, and with the chemical reaction, the zinc layer on the

Hot-dip galvanized wire has longer service life and better corrosion resistance than ordinary steel wire. Hot dip galvanizing is a method of chemical

The quality of hot-dip galvanized barbed wire is only the zinc layer attached to the surface of the wire, and with the chemical reaction, the zinc layer on the

Hot dip galvanizing is to remove oil from the workpiece, pickling, dipping, drying after dipping into the dissolved zinc solution for a certain time, can be

Hot dip galvanized wire is used in carbon structural steel, which is processed by drawing and hot dip galvanized. It is widely used in the manufacture of wire

Friends in the industry know that galvanized iron wire has two kinds of cold galvanized iron wire and hot galvanized iron wire, so what is the difference

1. Electroplating process control The service condition and service life of electro galvanized iron wire or component are closely related to the thickness of

In order to make the zinc content of steel wire stable in the future, and maintain its uniformity, as far as possible to reduce the zinc content, and

Hot dip galvanizing is a kind of external treatment technology in the production of fasteners. The common varieties of hot dip galvanizing fasteners are

The hot plating wire is made of low carbon steel wire rod, which is processed by drawing forming, pickling and rust removal, high temperature annealing, hot dip

1. Zinc pot operators must stick to their posts Zinc pot workers should be determined to do duty and responsibility. Do not leave the post without leave,

The quality of hot-dip galvanized barbed wire is only good in the surface of the wire attached to the galvanized layer, and with the chemical reaction, the

The hot plating wire is made of low carbon steel wire rod, which is processed by drawing forming, pickling and rust removal, high temperature annealing, hot dip

Out-of-line annealing means that the recrystallization annealing of hot or cold rolled steel plate is carried out in the bottom type annealing furnace or cover

Every galvanized wire production into the peak season of the industry, the road to the factory will from time to time see transportation wire and container

Most people in addition to pay attention to the price of barbed rope, many people for hot-dip galvanized barbed rope or cold galvanized barbed rope will have

The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color

1. Eliminate caked zinc residue on zinc liquid surface With a large pickpocket used for steel wire, into the zinc liquid before the surface of the zinc ash

1. Zinc pot operators must stick to their posts Zinc pot workers should be determined to do duty and responsibility. Do not leave the post without leave,

Hot dip galvanizing is to remove oil from the workpiece, pickling, dipping, drying after dipping into the dissolved zinc solution for a certain time, can be